FERROFLO® SPS05PK02NA
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Ferro Corporation |
| Trademark: | FERROFLO® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Uw8hSk_FERROFLO-SPS05PK02NA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FERROFLO®SPS05PK02NA is a high impact polystyrene material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. FERROFLO®The main characteristics of the SPS05PK02NA are: lubrication. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 35 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 72 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 22.1 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 30 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% secant : 23°C | 1720 | MPa | ASTM D790 |
| Tangent : 23°C | 1860 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 31.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 3.18 mm) | 270 | J/m | ASTM D256 |
| Dart Drop Impact (23°C) | 1.81 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 79.4 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 68.3 | °C | ASTM D648 |
| Additional Information |
|---|
| The value listed as Unnotched Izod Impact, ASTM D256, was tested in accordance with ASTM D4812.Silicone Content, Compuglass: 5% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Restramid PA 6 15GF | Polimarky Spolka Jawna | Nylon 6 | Restramid |
| SEETEC LDPE XL610 | Lotte Chemical Corporation | LDPE | SEETEC LDPE |
| Wellamid® MRGF30/10 42H-GY1 | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| Formolene® HB5202A | Formosa Plastics Corporation, U.S.A. | HDPE Copolymer | Formolene® |
| Jiangsu Sinarise JM8831 | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |