POLYfill PP CIP6020F
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Polykemi AB |
| Trademark: | POLYfill |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Uvluwz_POLYfill-PP-CIP6020F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Mineral reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.1 to 1.4 | % | |
| Flow | 1.1 to 1.4 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 21.0 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 2000 | MPa | ISO 178 |
| Flexural Stress | 35.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | 3.0 | kJ/m² | |
| -20°C | 3.5 | kJ/m² | |
| 23°C | 25 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, Unannealed | 129 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 67.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 145 | °C | ISO 306/A50 |
| -- | 66.0 | °C | ISO 306/B50 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® C 218 V40 BLACK 21 | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| DILAMID® 66 SV 30 NATURAL OR BLACK | Dilaplast S.p.A. | Nylon 66 | DILAMID® |
| FERREX® GPP20CC56HB BLUE | Ferro Corporation | PP Homopolymer | FERREX® |
| ELASTOSIL® R 510/60 | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| LNP™ COLORCOMP™ 143C compound | SABIC Innovative Plastics | PC | LNP™ COLORCOMP™ |