LNP™ THERMOCOMP™ ZX08005 compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UuwskW_LNPTHERMOCOMPZX08005compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP ZX08005 is a Compound based on PPE + PS Blend resin, containing Mineral. Added features include: Improved Dielectric Properties. Also known as: LNP* THERMOCOMP* Compound ZX08005 Product reorder name: ZX08005 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.07 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 55.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 4.4 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 4600 | MPa | ISO 178 |
| Flexural Stress | 105 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 17 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 140 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 130 | °C | ASTM D648 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Relative Permittivity | IEC 60250 | ||
| 100 MHz | 6.58 | IEC 60250 | |
| 500 MHz | 6.47 | IEC 60250 | |
| 1.00 GHz | 6.16 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 MHz | 1.0E-3 | IEC 60250 | |
| 500 MHz | 1.0E-3 | IEC 60250 | |
| 1.00 GHz | 1.0E-3 | IEC 60250 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 277 - 288 | °C | |
| Middle Temperature | 288 - 299 | °C | |
| Front Temperature | 299 - 310 | °C | |
| Processing (Melt) Temp | 299 - 304 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax RP482V | LyondellBasell Industries | PP Random Copolymer | Pro-fax |
| Spartech Polycom SC1-3090 | Spartech Polycom | ABS | Spartech |
| Zhongfa PP pp8 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| AKROMID® B3 natural (2500) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| HiFill FR® PA6/6 GF35 FR-N BK | Techmer Engineered Solutions | Nylon 66 | HiFill FR® |