Moplen 2152HOXP
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Utglel_Moplen-2152HOXP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Moplen 2152HOXP is Basell's latest innovative core development grade, specifically designed for very high speed production of BOPP films. It can be used in plain and coex film structures, providing an easy film stretchability, an improved thickness profile and very good compatability with the skin layer resin. Moplen 2152HOXP shows an excellent processability / film properties balance and good film optics. Moplen 2152HOXP does not contain any slip or antistatic agents and it is Calcium Stearate free. The product is suitable for metallization purposes. Typical applications are packaging of foodstuffs, cosmetics and videocasettes. For regulatory information please refer to Moplen 2152HOXP Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 71 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1480 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 35.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 10 | % | ISO 527-2/50 |
| Fracture | 290 | % | ISO 527-2/50 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Tangent (20 µm) | 2650 | MPa | MA 18068 |
| Tensile Stress 1(Break, 20 µm) | 127 | MPa | MA 18068 |
| Tensile Elongation 2(Break, 20 µm) | 29 | % | MA 18068 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 93.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 152 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (20.0 µm) | 0.40 | % | ASTM D1003 |
| Additional Information |
|---|
| Typical Film Properties of monolayer film produced on T.M. Long equipment, a laboratory simultaneous film stretcher (7x7@150°C) |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PROTEQ™ H16ST6 | Marplex Australia Pty. Ltd. | PP Homopolymer | PROTEQ™ |
| Sinvicomp SRF3705B | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| TERRAMAC TE-1070 | UNITIKA Plastics Division | PLA | TERRAMAC |
| DURANEX® CRN7000GP | Polyplastics Co., Ltd. | PBT | DURANEX® |
| LEXAN™ XHT2146 resin | SABIC Innovative Plastics | PC | LEXAN™ |