AIE PP 8010HMS-TFHI
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Asia International Enterprise (Hong Kong) Limited |
| Trademark: | AIE PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ur88V8_AIEPP8010HMSTFHI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Materials Features: It is suitable for hot-plate welding. It has high melt flow stregth and high sag resistance. It can be made into products of semi-transparent, low temperature resistance, impact resistance materials for automotive, motorcycle carbon canister housings, automotive expansion tank, accumulator case, power battery cases and other parts that require for hot-plate welding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 0.910 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.5 | % | ASTM D955 |
| Transverse flow | 1.7 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | 23.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | > 160 | % | ASTM D638 |
| Flexural Modulus 4 | 700 | MPa | ASTM D790 |
| Flexural Strength 5 | 27.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | 500 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 74.0 | °C | ASTM D648 |
| Melting Temperature | 170 | °C | DSC |
| CLTE - Flow (-20 to 150°C) | 5.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.10 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.6 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 3.0 mm/min |
| 5 . | 3.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® GW350 NT | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| UBESTA 3035 JU5 | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| Exelene® LLDPE 2401 | Montachem International, Inc. | LLDPE | Exelene® LLDPE |
| Formolene® E925 | Formosa Plastics Corporation, U.S.A. | HDPE, HMW | Formolene® |
| Lucky Enpla LAY1004EX | Lucky Enpla Co LTD | PC+ABS | Lucky Enpla |