ALCUDIA® EBA PA-1303
| Category: | EBA , Ethylene Butyl Acrylate Copolymer |
| Manufacturer: | REPSOL |
| Trademark: | ALCUDIA® EBA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UoxrkC_ALCUDIA-EBA-PA-1303.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EBA ALCUDIA® PA-1303 is a copolymer suitable for blown film applications where good flexibility and very good mechanical properties are required. The butyl acrylate content is 13%. TYPICAL APPLICATIONS
Recommended melt temperature 180°C. Processing characteristics of PA-1303 are similar to LDPE and conventional polyethylene extruders are recommended. Processing conditions should be optimised for each production line. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.925 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.30 | g/10 min | ISO 1133 |
| n-Butyl Acrylate Content | 13.0 | wt% |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 1.3 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 200 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Fracture, 200 µm, blown film | 20.0 | MPa | ISO 527-3 |
| TD : Fracture, 200 µm, blown film | 22.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Fracture, 200 µm, blown film | 570 | % | ISO 527-3 |
| TD : Fracture, 200 µm, blown film | 600 | % | ISO 527-3 |
| Dart Drop Impact (200 µm, blown film) | > 1500 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 200 µm, blown film | 13 | N | ISO 6383-2 |
| TD : 200 µm, blown film | 13 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Melting Temperature | 101 | °C |
| Additional Information |
|---|
| Data taken from 200 µm thickness film, blow up ratio 1:2.5, frost line height 50 cm. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene FRP257-01 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Milastomer™ W750B | Mitsui Chemicals America, Inc. | TPV | Milastomer™ |
| Ultramid® A3HG7 | BASF Corporation | Nylon 66 | Ultramid® |
| Nypol® PA A3 T40 HS NTLA013 NR327 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| DINALON® B1S25 M404 | Grupo Repol | Nylon 6 | DINALON® |