Epocast 169A-1 / Hardener 9615
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Huntsman Advanced Materials |
| Trademark: | Epocast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UopHG6_Epocast-169A-1-Hardener-9615.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DESCRIPTION: Epocast® 169A-1 Resin / 9615 Hardener is a two-component, low-density epoxy syntactic which cures at room temperature to a carvable, wood-like product. The cured Epocast® 169A-1 Resin / 9615 Hardener system has good dimensional stability under changing humidity conditions. Epocast® 169A-1 Resin / 9615 Hardener is qualified to SS-9587, Type 1. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D1622 | ||
| -- 1 | 0.560 | g/cm³ | ASTM D1622 |
| -- 2 | 0.680 | g/cm³ | ASTM D1622 |
| -- 3 | 0.960 | g/cm³ | ASTM D1622 |
| Viscosity | ASTM D2196 | ||
| 25°C 4 | Paste | ASTM D2196 | |
| 25°C 5 | Semi-paste | ASTM D2196 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time - 100 gms (25°C) 6 | 1.0 - 2.0 | hr | ASTM D2471 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Lap Shear - AL/AL | 8.27 | MPa | ASTM D1002 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Strength | 21.4 | MPa | ASTM D695 |
| Shear Strength | 16.5 | MPa | ASTM D732 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Resin | Mixing ratio by weight: 100 | ||
| Hardening method | Mixing ratio by weight: 50 | ||
| Thermoset Mix Viscosity 7(25°C) | 35000 | cP | ASTM D2196 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CURE SCHEDULE: 3 days at 75°F ± 5°F (23°C ± 3°C), or room temperature gel plus 2 hours at 150°F ± 10°F (66°C ± 6°C). |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | System |
| 3 . | Hardener |
| 4 . | Resin |
| 5 . | System |
| 6 . | System |
| 7 . | Hardener |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 7868-70 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Nypol® PA A3 BGE0072 NR319 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| LNP™ THERMOCOMP™ WC006 compound | SABIC Innovative Plastics | PBT | LNP™ THERMOCOMP™ |
| Osterlene® HB6564 | Osterman & Company | HDPE | Osterlene® |
| LNP™ LUBRICOMP™ DFL36ELH compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |