LNP™ STAT-KON™ DD200C compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UonSdk_LNP-STAT-KON-DD200C-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PTFE free polycarbonate compounds with ESD safety and good lubricating perfomrance , suitable for Semiconductor and Hard Disk Drive (HDD) and semicon industry. Added features of this material include: Good cleanliness control, low LPC, low ionic, and low outgassing. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.22 | g/cm³ | ASTM D792 |
| -- | 1.20 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.50 to 0.70 | % | |
| Across Flow | 0.50 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2410 | MPa | ASTM D638 |
| -- | 2350 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 53.0 | MPa | ASTM D638 |
| Yield | 53.0 | MPa | ISO 527-2/5 |
| Break 3 | 46.0 | MPa | ASTM D638 |
| Break | 53.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 5.3 | % | ASTM D638 |
| Yield | 5.2 | % | ISO 527-2/5 |
| Break 5 | 10 | % | ASTM D638 |
| Break | 10 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- | 2200 | MPa | ASTM D790 |
| -- 6 | 2390 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 87.0 | MPa | ASTM D790 |
| -- | 87.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7(23°C) | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 92 | kJ/m² | ISO 179/2U |
| Notched Izod Impact | |||
| 23°C | 120 | J/m | ASTM D256 |
| 23°C 8 | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1800 | J/m | ASTM D4812 |
| 23°C 9 | 90 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 138 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 125 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+5 to 1.0E+9 | ohms | ASTM D257 |
| Static Decay 10 | 0.1 | sec | FTMS 101B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 80*10*4 sp=62mm |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 5000V to <50V |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1300 C AR 35 | RTP Company | PPS | RTP |
| TITANLENE® LDF 266YZ | Lotte Chemical Titan (M) Sdn. Bhd. | LDPE | TITANLENE® |
| Karina YELLOW PVC COMPOUND 701D02/ 23-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OLEFISTA™ QX0238C | Mitsubishi Chemical Performance Polymers, Inc. | Elastomer, Specialty | OLEFISTA™ |
| POFEX EP8300S 90M | POLYROCKS CHEMICAL CO., LTD | TPU, Unspecified | POFEX |