AKROMID® A3 1 S3 black (1139)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UoDkRm_AKROMID-A3-1-S3-black-1139-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 1 S3 black (1139) is an unreinforced, heat stabilised and dry impact resistant polyamide 6.6 Applications are connecting and fixing systems, used at elevated temperatures in the automotive and electro industry |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.10 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 80.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 2.2 | -- | % | |
| Flow | 2.1 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 2.1 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flexural Strain at Break 1 | 7.5 | -- | % | ISO 178 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Shore Hardness (Shore D, 23°C) | 75 | -- | DIN 53505 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2700 | 1300 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 63.0 | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | > 35 | > 100 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 2500 | -- | MPa | ISO 178 |
| Flexural Stress 3 | 90.0 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | 13 | kJ/m² | |
| 23°C | 17 | 25 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 12 | -- | kJ/m² | |
| -20°C | 12 | -- | kJ/m² | |
| 23°C | 15 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 213 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 4 | 262 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Niplene F40 AGR | Soredi S.p.a. | PP Homopolymer | Niplene |
| Nypol® PA A2 BGE0046 NR241 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| ACLAR® 11A (8 mil) | Honeywell | PCTFE | ACLAR® |
| Fainplast PVC HGKA 83 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Braskem PP DH357.01 | Braskem Europe GmbH | PP Homopolymer | Braskem PP |