Multilon® DN-3720F
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | TEIJIN LIMITED |
| Trademark: | Multilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Uo4MOg_Multilon-DN-3720F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC/ABS polymer alloy, Non-halogen type flame resistant series |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.34 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 4.00 mm | 0.30 to 0.50 | % | |
| Flow : 4.00 mm | 0.20 to 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 60.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 5.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 5400 | MPa | ISO 178 |
| Flexural Stress 2 | 100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 60 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 95.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 83.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 98.0 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 | ||
| Flow | 3.0E-5 | cm/cm/°C | |
| Transverse | 6.5E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm | V-1 | ||
| 1.30 mm | V-0 | ||
| 1.80 mm | 5VB |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Selvol™ 205 | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| Moplen EP348U | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Toler EVA 182 | Toler Chemical, Inc | EVA | Toler EVA |
| TUFNYL® SFM 24 NATURAL | SRF Ltd. | Nylon 6 | TUFNYL® |
| Kotex K-20MRA28 | Kotec Corporation | PC | Kotex |