VESTAMID® HTplus R1133
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Evonik Industries AG |
| Trademark: | VESTAMID® HTplus |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UmbDbT_VESTAMID-HTplus-R1133.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Glass-fiber reinforced polyphthalamide compound especially suitable for plastic and rubber composites. VESTAMID HTplus R1133 is a glass-fiber reinforced (30%), heat-stabilized polyphthalamide compound (PPA) especially suitable for the production of rubber and plastic composites. This process is patented by Evonik Degussa GmbH. Parts of VESTAMID HTplus R1133 can be directly bonded to rubber, e. g., HNBR or FPM, without using any adhesives or adhesion promotors. This compound is especially suited for manufacturing parts subjected to high temperature. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.40 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 145 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C, Complete Break | 7.0 | kJ/m² | |
| 23°C, Complete Break | 6.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -40°C, Complete Break | 21 | kJ/m² | |
| 23°C, Complete Break | 28 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 296 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 244 | °C | ISO 75-2/A |
| Melting Temperature 1 | 300 to 315 | °C | ISO 11357 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | > 4.0 | hr |
| Note Message | |
|---|---|
| 1 . | 2nd Heating |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXT PCR PA66 G13-300PCR | NEXT Specialty Resins, Inc. | Nylon 66 | NEXT PCR |
| Boda BDT-LB3752 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| EVICOM™ RC7/539 | INEOS Compounds | PVC, Flexible | EVICOM™ |
| FERREX® GPP30CN33HB-NA | Ferro Corporation | PP, Unspecified | FERREX® |
| Elastocon® 8058BL | Elastocon TPE Technologies | TPE | Elastocon® |