G-PAEK™ 1230CF
| Category: | PEK , Polyether Ketone |
| Manufacturer: | Gharda Chemicals Ltd. |
| Trademark: | G-PAEK™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Um8F9r_G-PAEK-1230CF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Details: Ultra high performance thermoplastic polymer, 30% carbon fiber reinforced in Polyether Ketone, semi-crystalline granules suitable for injection molding, easy flow, Black in color. Application Areas: Suitable for high temperature applications, where higher strength & stiffness in load- bearing application is required. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | |
| Molding Shrinkage 1 | |||
| Flow | 0.10 | % | |
| Across Flow | 0.60 | % | |
| Water Absorption (Equilibrium) | 0.040 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale, 23°C) | 108 | ASTM D785 | |
| Durometer Hardness (Shore D, 23°C) | 91 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 28600 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 265 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 2.0 to 3.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 28.0 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 410 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 65 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 355 | °C | ASTM D648 |
| Continuous Use Temperature | 280 | °C | UL 746B |
| Glass Transition Temperature | 152 | °C | ASTM D3418 |
| Melting Temperature | 372 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+6 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Nozzle Temperature | 420 | °C | |
| Processing (Melt) Temp | 390 to 420 | °C | |
| Mold Temperature | 200 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | 420°C nozzle, 220°C Mold |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Milastomer™ S-650BS | Mitsui Chemicals America, Inc. | TPV | Milastomer™ |
| TEKAMID™ H24WC | Mando Advanced Materials Co., Ltd. | ABS+Nylon | TEKAMID™ |
| LEXAN™ LGK4030 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| PARAPET GH-SN | Kuraray Co., Ltd. | Acrylic (PMMA) | PARAPET |
| PLANAC BT-2230-60 | TOYOBO America, Inc. | PBT | PLANAC |