LEXAN™ LUX2910T resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Um7O87_LEXAN-LUX2910T-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Global grade. LEXAN LUX2910T is an injection molding grade especially designed for manufacturing optical parts requiring superior flow properties combined with very high transmission and color stability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 58 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow 1 | 0.60 to 0.90 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 2 | 2230 | MPa | ASTM D638 |
| Tensile Strength 3 | ASTM D638 | ||
| Yield | 61.0 | MPa | |
| Break | 59.0 | MPa | |
| Tensile Elongation 4 | ASTM D638 | ||
| Yield | 7.0 | % | |
| Break | 120 | % | |
| Flexural Modulus 5(50.0 mm Span) | 2420 | MPa | ASTM D790 |
| Flexural Strength 6(Yield, 50.0 mm Span) | 97.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 44 | J/m | |
| 23°C | 580 | J/m | |
| Unnotched Izod Impact (23°C) | 2100 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 56.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 139 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 124 | °C | |
| Vicat Softening Temperature | 142 | °C | ISO 306/B120 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 95°C | 6.8E-5 | cm/cm/°C | |
| Transverse : -40 to 95°C | 6.6E-5 | cm/cm/°C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2540 µm) | > 90.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 271 to 293 | °C | |
| Middle Temperature | 282 to 304 | °C | |
| Front Temperature | 293 to 316 | °C | |
| Nozzle Temperature | 288 to 310 | °C | |
| Processing (Melt) Temp | 293 to 316 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propak® 7021 | PolyPacific Pty. Ltd. | PP Homopolymer | Propak® |
| Taitacell EPS 351SA | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| Vibrathane® B836 | Chemtura | PUR-Ether/MDI | Vibrathane® |
| En Chuan 6021ALC | En Chuan Chemical Industries Co,. Ltd. | Polyester, TS | En Chuan |
| Hyundai EP PA6 LS165 | HYUNDAI EP Co., Ltd. | Nylon 6 | Hyundai EP PA6 |