SABIC® PP CX04-82
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ulrm1N_SABIC-PP-CX04-82.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PP CX04-82 is an emission optimised high flowing high crystalline copolymer. Its very high flow and highly isotropic behaviour permits fast cycle-times and injection moulding of large articles demanding low warpage and high dimensional stability. Typical applications are automotive interior components. SABIC® PP CX04-82 is a designated automotive grade |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 40 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 24 hr | 1.4 | % | |
| 24 hr | 1.4 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 64 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant : Injection Molded 1 | 1600 | MPa | ASTM D638 |
| Injection Molded | 1500 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield, Injection Molded 2 | 26.0 | MPa | ASTM D638 |
| Yield, Injection Molded | 26.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield, Injection Molded 3 | 4.0 | % | ASTM D638 |
| Yield, Injection Molded | 4.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0°C, Injection Molded | 6.0 | kJ/m² | |
| 23°C, Injection Molded | 8.0 | kJ/m² | |
| Notched Izod Impact | |||
| -20°C, Injection Molded | 50 | J/m | ASTM D256A |
| 0°C, Injection Molded | 70 | J/m | ASTM D256A |
| 23°C, Injection Molded | 90 | J/m | ASTM D256A |
| -20°C, Injection Molded | 4.0 | kJ/m² | ISO 180/1A |
| 0°C, Injection Molded | 6.0 | kJ/m² | ISO 180/1A |
| 23°C, Injection Molded | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 150 | °C | ASTM D1525, ISO 306/A120 4 4 |
| -- | 78.0 | °C | ASTM D1525, ISO 306/B120 5 5 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission | < 50.0 | µgC/g | VDA 277 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | Rate B (120°C/h), Loading 1 (10 N) |
| 5 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Chemical Resources BPP3500 | Chemical Resources, Inc. | PP Impact Copolymer | Chemical Resources |
| ColorFast® PCGF120 | LTL Color Compounders, Inc. | PC | ColorFast® |
| HiFill® PA6/6 GF13 IM2 HS L | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| LNP™ LUBRICOMP™ FX04491H compound | SABIC Innovative Plastics | PE, Unspecified | LNP™ LUBRICOMP™ |
| TOTAL Polypropylene PPC 5948WZ | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |