Braskem PE IA-59 U3
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UliQd5_Braskem-PE-IA-59-U3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
IA59U3 is a High Density Polyethylene, narrow molecular weight homopolymer, produced by solution process for injection moulding applications. It offers high stiffness and impact strength, combined with good processability and low warpage. It contains light stabilizer and antioxidant additive. Application: Crates, cases, containers, pails, pallets and technical articles which require high weathering resistance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.960 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 7.3 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | ASTM D1693 | ||
| 50°C, 2.00 mm, 10% Igepal, Compression Molded, F50 | < 3.00 | hr | |
| 50°C, 2.00 mm, 100% Igepal, Compression Molded, F50 | < 3.00 | hr |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 58 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, Compression Molded | 28.0 | MPa | |
| Break, Compression Molded | 25.0 | MPa | |
| Flexural Modulus - 1% Secant (Compression Molded) | 1300 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 73 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Compression Molded) | 81.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 129 | °C | ASTM D1525 1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 160 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Braskem PE LD 5000A | Braskem | LDPE | Braskem PE |
| Kynar Ultraflex® B | Arkema | PVDF | Kynar Ultraflex® |
| Karina IVORY PVC COMPOUND 750-35/1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Petrotene® PP A3 C35 BRC0001 PH383 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |
| LNP™ LUBRICOMP™ Lexan_LF1530A compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |