LNP™ THERMOCOMP™ JF004E compound
| Category: | PESU , Polyethersulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UlG2GG_LNPTHERMOCOMPJF004Ecompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP JF004E is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Easy Molding. Also known as: LNP* THERMOCOMP* Compound JF-1004 EM Product reorder name: JF004E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.50 - 0.70 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.60 - 0.80 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.60 - 0.80 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.50 - 0.70 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.40 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 7360 | MPa | ASTM D638 |
| -- | 7590 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 114 | MPa | ASTM D638 |
| Fracture | 109 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 2.9 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 6690 | MPa | ASTM D790 |
| -- | 7590 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 186 | MPa | ASTM D790 |
| -- | 183 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 2 | 7.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 430 | J/m | ASTM D4812 |
| 23°C 3 | 73 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 16.0 | J | ASTM D3763 |
| -- | 4.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 206 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 205 | °C | ISO 75-2/Af |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPR 6298 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| Xuchuan A-7150/B-8260 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| Osterlene® HI-9-2.6-stg | Osterman & Company | PS (HIPS) | Osterlene® |
| KMI PP KM-0284ZW | KMI Group, Inc. | PP Impact Copolymer | KMI PP |
| Durethan® BM 240 H2.0 901510 | LANXESS Corporation | Nylon 6 | Durethan® |