LNP™ THERMOCOMP™ DZ004 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UlEoGp_LNP-THERMOCOMP-DZ004-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP DZ004 is a compound based on Polycarbonate resin containing 20% Milled Glass. Also known as: LNP* THERMOCOMP* Compound DF-1004 M Product reorder name: DZ004 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (24 hr) | 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3700 | MPa | ASTM D638 |
| Tensile Strength (Break) | 60.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.5 | % | ASTM D638 |
| Flexural Modulus | 3510 | MPa | ASTM D790 |
| Flexural Strength | 96.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1100 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 136 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2700 S-30A | RTP Company | SEBS | RTP |
| 3M™ Dyneon™ PTFE Compound TF 3311 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Elastron® G G100.A80.B | Elastron USA, Inc. | SEBS | Elastron® G |
| Karina CLEAR PVC COMPOUND -E 80/202-D-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TechnoFiber PP LGF 60-10-01 H | TechnoCompound GmbH | PP, Unspecified | TechnoFiber |