KPOL-HDPE HD K-7.0/950

Category:	HDPE, EHMW , High Density (EHMW) Polyethylene
Manufacturer:	KPOL Chem Co.
Trademark:	KPOL-HDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Ul9Kid_KPOL-HDPE-HD-K-7-0-950.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

High Density Polyethylene Extra high molecular weight, hexene copolymer Extrusion-Blow Molding

Characteristics

The KPOL HD K-7.0/950; is a high molecular weight high-density polyethylene, copolymer.

Offers good processability, outstanding stress cracking resistance (ESCR), excellent stiffness and impact strength. Suitable for blow molding of large volumes and Sheet extrusion to guard buckets pickup (bedliner).

Applications

Typical blow molded applications include containers and drums from 20 to 200 liters, for chemical, agrochemical and food package, small tanks and bedliner, Pallets, Automotive dunnage, Truck bedliners.

The KPOL® resin meets the requirements of section 177.1520, paragraph C, from chapter 21 denominated "Olefin Polymers" from the Code of Federal Regulations of the FDA, to be utilized with direct food contact.

General Information
Additive	Antioxidant
Features	Antioxidant Copolymer Food Contact Acceptable Good Processability Hexene Comonomer High Density High ESCR (Stress Crack Resist.) High Impact Resistance High Molecular Weight High Stiffness
Uses	Automotive Applications Drums Food Packaging Industrial Tanks Tanks
Agency Ratings	FDA 21 CFR 177.1520(c)
Processing Method	Blow Molding Extrusion Sheet Extrusion

Physical	Nominal Value	Unit	Test Method
Density	0.950	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/21.6 kg)	7.0	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance ¹
50°C, 1.91 mm, 10% Igepal CO-630	200	hr	ASTM D1693B
50°C, 3.18 mm, 100% Igepal CO-630	> 650	hr	ASTM D1693A

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	68		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield)	32.0	MPa	ASTM D638
Tensile Elongation (Break)	700	%	ASTM D638
Flexural Modulus - Tangent	1.25	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Tensile Impact Strength	195	kJ/m²	ASTM D1822

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	< -77.0	°C	ASTM D746
Vicat Softening Temperature	125	°C	ASTM D1525
Melting Temperature	132	°C	DSC
Heat Deflection Temperature	74	°C	ASTM D648

Note Message
1 .	Grooved Specimen

Resin Grade	Manufacturer	Category	Trademark
POLYLAC® PA-757G J08	CHI MEI CORPORATION	ABS	POLYLAC®
Moplen EP240T	LyondellBasell Industries	PP Impact Copolymer	Moplen
DOW™ Electrical & Telecommunications GP K-6050 NT	The Dow Chemical Company	LLDPE	DOW™ Electrical & Telecommunications
LNP™ LUBRICOMP™ RX85514 compound	SABIC Innovative Plastics	Nylon 66	LNP™ LUBRICOMP™
Zetpol® 2010	Zeon Corporation	NBR	Zetpol®