LubriOne™ NN-20GF-10GB/13T-2S BLACK
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | LubriOne™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ul8CwW_LubriOne-NN-20GF-10GB-13T-2S-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 9650 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 117 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 1.0 to 3.0 | % | ASTM D638 |
| Flexural Modulus | 6230 | MPa | ASTM D790 |
| Flexural Strength | 172 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Metal - Dynamic | 0.59 | ||
| vs. Steel - Static | 0.46 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.35 mm, Injection Molded) | 64 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed, 3.18 mm) | 239 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| 3 . | Type I, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® 1521AH | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| Safrene® M 5010NAT80 | Safripol (PTY) LTD | HDPE | Safrene® |
| Spartech Polycom SC2-1090U | Spartech Polycom | PS (HIPS) | Spartech |
| Formolene® 1102KR | Formosa Plastics Corporation, U.S.A. | PP, High Crystal | Formolene® |
| TECHNYL® A 118 V50 BLACK 21 | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |