TAISOX 2110
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAISOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ul4auw_TAISOX-2110.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TAISOX 2110 is a linear low density polyethylene material,. This product is available in North America, Europe or Asia Pacific region. The processing method is blow molded film. The main features of TAISOX 2110 are:
The typical application fields of TAISOX 2110 are: movies |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 38 µm, blown film | 157 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm, blown film | 196 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm, blown film | 9.81 | MPa | ASTM D882 |
| TD : Yield, 38 µm, blown film | 10.8 | MPa | ASTM D882 |
| MD : Broken, 38 µm, blown film | 49.0 | MPa | ASTM D882 |
| TD : Broken, 38 µm, blown film | 44.1 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 620 | % | ASTM D882 |
| TD : Broken, 38 µm, blown film | 810 | % | ASTM D882 |
| Dart Drop Impact (38 µm, Blown Film) | 610 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, blown film | 460 | g | ASTM D1922 |
| TD : 38 µm, blown film | 760 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 93.0 | °C | ASTM D1525 |
| Melting Temperature | 121 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm, Blown Film) | 51 | ASTM D2457 | |
| Clarity | 65.0 | ASTM D1746 | |
| Haze (38.0 µm, Blown Film) | 13 | % | ASTM D1003 |
| Additional Information |
|---|
| Blow Up Ratio: 2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris ABS LER572 | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| TOTAL Polystyrene Impact 975E | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| Toraycon® 1154W | Toray Resin Company | PBT | Toraycon® |
| Westlake LDPE EF412 | Westlake Chemical Corporation | LDPE | Westlake LDPE |
| Jiangsu Sinarise PI90001X | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |