Keyflex® BT 1035D
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Keyflex® BT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UioSie_Keyflex-BT-1035D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description General Purpose, Low Modulus Application Automotive Interior, Soft Touch Grips |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.80 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.70 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A | 88 | ||
| Shore D | 33 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break, 2.00 mm) | 19.6 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 2.00 mm) | 750 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 6.40 mm | No Break | ||
| 23°C, 6.40 mm | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 165 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (CTI) 3 | 600 | V | UL 746 |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 170 to 190 | °C | |
| Middle Temperature | 180 to 200 | °C | |
| Front Temperature | 190 to 210 | °C | |
| Nozzle Temperature | 190 to 210 | °C | |
| Processing (Melt) Temp | 165 to 205 | °C | |
| Mold Temperature | 10.0 to 35.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Cylinder Zone 1 Temp. | 170 to 190 | °C | |
| Cylinder Zone 2 Temp. | 180 to 200 | °C | |
| Cylinder Zone 3 Temp. | 180 to 200 | °C | |
| Cylinder Zone 4 Temp. | 180 to 200 | °C | |
| Adapter Temperature | 180 to 200 | °C | |
| Melt Temperature | 165 to 205 | °C | |
| Die Temperature | 180 to 200 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | Solution A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE Powder 1922P3 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| Sylvin 9664-57 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| THERMOLAST® K TF3BTL (Series: FC/AP) | KRAIBURG TPE | TPE | THERMOLAST® K |
| ELITE™ 5811 | The Dow Chemical Company | EPE | ELITE™ |
| LONGLITE® PBT 3030-104XR | CCP Group | PBT | LONGLITE® PBT |