ACCULOY™ POL063L
| Category: | PC+PET , Polycarbonate + PET |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCULOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UigiXh_ACCULOY-POL063L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCULOY™ POL063L is a Polycarbonate + PET (PC+PET) product. It is available in North America. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1700 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 59.0 | MPa | |
| Break | 60.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 68 | % | |
| Break | 150 | % | |
| Flexural Modulus | 2500 | MPa | ASTM D790 |
| Flexural Strength | 88.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 1000 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 126 | °C | |
| 1.8 MPa, Unannealed | 107 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CGPC PVC R-11X NI Extrusion | China General Plastics Corporation | PVC, Flexible | CGPC PVC |
| Hanwha Total PE EP30 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | LLDPE | Hanwha Total PE |
| HiFill FR® ABS FR UV | Techmer Engineered Solutions | ABS | HiFill FR® |
| LEXAN™ FL905 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| LUVOCOM® 1/CF/20/TF/5 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |