CALIBRE™ 302EP-35
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ui3NKM_CALIBRE-302EP-35.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 302EP-35 is a high flow, UV stabilized polycarbonate resin with excellent heat resistance and optical clarity. Main Characteristics
Applications
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 35 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.32 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 62.1 | MPa | |
| Break | 48.3 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 5.7 | % | |
| Break | 81 | % | |
| Flexural Modulus 3 | 2450 | MPa | ASTM D790 |
| Flexural Strength 4 | 95.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 640 | J/m | ASTM D256 |
| Instrumented Dart Impact 5(23°C, Total Energy) | 62.1 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 137 | °C | |
| 1.8 MPa, Unannealed | 122 | °C | |
| Vicat Softening Temperature | 146 | °C | ASTM D1525 6 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (1000 µm) | 89.0 | % | ASTM D1003 |
| Haze (1000 µm) | 0.60 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 3.39 m/sec |
| 6 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DOW鈩?LDPE 219M | The Dow Chemical Company | LDPE | DOW鈩?LDPE |
| Flexathene® TP38NC01X01 | LyondellBasell Industries | Polyolefin, Unspecified | Flexathene® |
| Hifax ETA3104 | LyondellBasell Industries | TPO (POE) | Hifax |
| Lupoy® NS5000 | LG Chem Ltd. | PC+ABS | Lupoy® |
| PERLER® N09X4002B01 | A.D. Compound S.p.A. | PP Homopolymer | PERLER® |