LNP™ THERMOCOMP™ JF006 compound
| Category: | PESU , Polyethersulfone |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UhCYyE_LNPTHERMOCOMPJF006compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP JF006 is a compound based on Polyethersulfone resin containing 30% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound JF-1006 Product reorder name: JF006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.58 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.30 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.50 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.48 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.27 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.34 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.46 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10800 | MPa | ASTM D638 |
| -- | 9450 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 143 | MPa | ASTM D638 |
| Fracture | 136 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 2.2 | % | ASTM D638 |
| Fracture | 2.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 9720 | MPa | ASTM D790 |
| -- | 10000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 210 | MPa | ASTM D790 |
| -- | 208 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.52 | ASTM D3702 Modified | |
| With Self-Static | 0.57 | ASTM D3702 Modified | |
| Wear Factor - Washer | 170 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 96 | J/m | ASTM D256 |
| 23°C 2 | 9.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 610 | J/m | ASTM D4812 |
| 23°C 3 | 40 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 10.7 | J | ASTM D3763 |
| -- | 4.16 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 210 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 210 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 3.1E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 3.6E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 3.7E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 343 - 354 | °C | |
| Middle Temperature | 360 - 371 | °C | |
| Front Temperature | 371 - 382 | °C | |
| Processing (Melt) Temp | 354 - 371 | °C | |
| Mold Temperature | 138 - 149 | °C | |
| Back Pressure | 0.344 - 0.689 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ProtoCast 19122 | DSM Somos® | Unspecified | ProtoCast |
| DURANEX® 702MS | Polyplastics Co., Ltd. | PC+PBT | DURANEX® |
| Ebalta AH 100 / TGS | Ebalta Kunststoff GmbH | Epoxy | Ebalta |
| MAJORIS FFR020X | AD majoris | PP, Unspecified | MAJORIS |
| Sylvin 3290-60 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |