OP - PEI 20GF
| Category: | PEI , Polyether Imide |
| Manufacturer: | Oxford Polymers |
| Trademark: | OP - PEI |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UhBnal_OP---PEI-20GF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| OP-PEI 20GF is a polyetherimide (PEI) material, and the filler is 20% glass fiber reinforced material. This product is available in North America,. The main characteristics of OP-PEI 20GF are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 14 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 - 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 138 | MPa | ASTM D638 |
| Fracture | 138 | MPa | ASTM D638 |
| Flexural Modulus | 6140 | MPa | ASTM D790 |
| Flexural Strength | 200 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (4°C) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 210 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 207 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | V-0 | UL 94 | |
| 3.18 mm | V-0 | UL 94 |
| Additional Information |
|---|
| Melt Mass - Flow Rate (MFR), ASTM D1238, 190°C/ 2.16kg: 5 to 22 g/10min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 143 - 149 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Rear Temperature | 332 - 399 | °C | |
| Middle Temperature | 338 - 399 | °C | |
| Front Temperature | 343 - 399 | °C | |
| Processing (Melt) Temp | 338 - 399 | °C | |
| Mold Temperature | 107 - 177 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V900 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| AMTOPP AA20 | Inteplast Group | PP, Unspecified | AMTOPP |
| LEXAN™ IR1810 resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| Karina CLEAR PVC COMPOUND 80/224-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sumiliteresin® PR-51206 | SBHPP | Phenolic | Sumiliteresin® |