Desmovit® DP R 3932

Category:	TPU-Ester/Ether , Thermoplastic Polyurethane Elastomer (Ester/Ether)
Manufacturer:	geba Kunststoffcompounds GmbH
Trademark:	Desmovit®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Uh5IZ8_Desmovit-DP-R-3932.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Ester-based injection molding type with a ratio of 20% glass fiber

Characteristics:

high level of mechanical strength, good flexibility at low temperature, good noise absorption, very good colorability and printability, excellent heat & oil resistance, high abrasion resistance, easy to bond

Applications:

Shoe soles, shin guards, midsoles for special shoes, standard automotive applications such as: brackets, hot air intakes, side sills, shift knobs, roof rails, front spoiler, side shields, handles for walking sticks, controls, wear parts for agricultural machinery & harvester, industrial component construction, mechanical and tribologically highly stressed components in exterior use, technical units with low friction coefficients, cup holders, center console, skate roller core, role core chair, camping items.

General Information
Filler / Reinforcement	Glass Fiber, 20% Filler by Weight
Features	Bondability Excellent Printability Good Abrasion Resistance Good Colorability High Heat Resistance High Strength Low Temperature Flexibility Noise Damping Oil Resistant
Uses	Agricultural Applications Automotive Applications Construction Applications Industrial Applications Outdoor Applications Safety Equipment Safety Guards
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	1.38	g/cm³	ISO 1183/A
Molding Shrinkage
Across Flow	0.16	%
Flow	0.58	%

Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D)	72		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress	83.0	MPa	ISO 527-2/200
Tensile Strain (Break)	11	%	ISO 527-2/200
Flexural Modulus ¹			ISO 178
-30°C	6220	MPa
23°C	3200	MPa
Flexural Stress ²			ISO 178
-30°C	227	MPa
23°C	99.0	MPa
Abrasion	61	mm³	ISO 4649

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C	9.0	kJ/m²
23°C	24	kJ/m²
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	60	kJ/m²
23°C	92	kJ/m²

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	159	°C	ISO 75-2/B
1.8 MPa, Unannealed	130	°C	ISO 75-2/A
Vicat Softening Temperature	146	°C	ISO 306/B50
CLTE			DIN 53752
Flow	2.1E-5	cm/cm/°C
Transverse	1.3E-4	cm/cm/°C

Injection	Nominal Value	Unit
Drying Temperature - Dry Air Dryer	120	°C
Drying Time	4.0	hr
Processing (Melt) Temp	220 to 245	°C
Mold Temperature	40.0 to 80.0	°C

Note Message
1 .	1.0 mm/min
2 .	2.0 mm/min

Resin Grade	Manufacturer	Category	Trademark
REPOL® H200FG	Reliance Industries Limited	PP Homopolymer	REPOL®
Indothene HD 46GP009	Reliance Industries Limited	HDPE	Indothene HD
ICORENE® 4140	ICO Polymers SA, A Division of A. Schulman	PE Copolymer	ICORENE®
LNP™ LUBRICOMP™ RFI12 compound	SABIC Innovative Plastics	Nylon 66	LNP™ LUBRICOMP™
POLYCOMPO PE 4020L	POLYCOMPO Co.,Ltd.	LLDPE	POLYCOMPO PE