Braskem PE EF2222
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Uh32TF_Braskem-PE-EF2222.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EF2222 is a low-density polyethylene (LDPE), with excellent processability and low gel content. Those features allow production of thin and highly uniform films. Additives: No additives Application: Smooth or embossed films for diapers, disposable sheets, etc. Films for lamination. Injection-Blow Molding. Foamed applications. Process: Recommended processing conditions for film extrusion about 145 - 190 °C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.922 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.2 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 38 µm | 170 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm | 210 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture, 38 µm | 30.0 | MPa | ASTM D882 |
| TD : Fracture, 38 µm | 20.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 38 µm | 420 | % | ASTM D882 |
| TD : Fracture, 38 µm | 1100 | % | ASTM D882 |
| Dart Drop Impact 1(38 µm) | 70 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm | 480 | g | ASTM D1922 |
| TD : 38 µm | 150 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 38.0 µm) | 100 | ASTM D2457 | |
| Haze | 6.0 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Recommended Blow Film Extrusion Conditions: Temperature Profile: 145°C to 190°C Mass Temperature: 190°C Blow up Ratio: 2.0 to 3.0 : 1 Die Gap: 1.0 mm |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-8451 BLK 940 | Teknor Apex Company | TPE | Telcar® |
| MOSTEN MA 611 | UNIPETROL RPA | PP Copolymer | MOSTEN |
| Ad-Tech Polyester NO. 38 | Ad-Tech Plastic Systems Corp. | Polyester, TS | Ad-Tech Polyester |
| Hostacom X 4305 HL86 C1V301 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Kinta NB6040G | Kinta Technology (Hong Kong) Co., Ltd. | Nylon 6 | Kinta |