Maxxam™ CL2 GF/30 BLACK
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Maxxam™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Uggg3I_Maxxam-CL2-GF-30-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Impact modified, Good heat stability |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 - 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 70.0 | MPa | ASTM D638 |
| Flexural Modulus 2 | 5000 | MPa | ASTM D790 |
| Flexural Strength 3 | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 210 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 145 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Charge Decay Time - 12% RH, 5000 kV to 50 kV | 2777777853490.1 | hr | MIL B-81705C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 200 - 240 | °C | |
| Middle Temperature | 200 - 240 | °C | |
| Front Temperature | 200 - 240 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ResMart Ultra POM | ResMart | Acetal (POM) Copolymer | ResMart Ultra |
| Sunny® PC-PBT EN120 | Guangdong Shunde Shunyan New Material Co., Ltd. | PC+PBT | Sunny® |
| Texalan® 6 Series 672D | Austin Novel Materials Co. Ltd. | TPU-Ester/Ether | Texalan® 6 Series |
| ELASTOSIL® E 60 | Wacker Chemie AG | Silicone | ELASTOSIL® E |
| SQUARE® LIM1522-35A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |