VALOX™ SHF4960 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UfxM9Y_VALOXSHF4960resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VALOX Super high flow grade, 30% glass filled Flame retardant, High CTI, heat stabilized with mold release. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.64 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 6.00 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.25 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.070 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10000 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 110 | MPa | ISO 527-2/5 |
| Fracture | 110 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 1.8 | % | ISO 527-2/5 |
| Fracture | 1.8 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 8500 | MPa | ISO 178 |
| Flexural Stress | 165 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2(23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact 3 | ISO 180/1A | ||
| -30°C | 7.0 | kJ/m² | ISO 180/1A |
| 23°C | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(-30°C) | 36 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed, 64.0 mm Span) | 195 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 185 | °C | ISO 306/B50 |
| -- | 195 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : -40 to 40°C | 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | ||
| 0.800mm, in oil | 35 | kV/mm | IEC 60243-1 |
| 1.60mm, in oil | 25 | kV/mm | IEC 60243-1 |
| 3.20mm, in oil | 18 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 275 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm, Testing by SABIC) | V-0 | UL 94 | |
| Oxygen Index | 32 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (250°C, 1500 sec^-1) | 92.0 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 - 60.0 | °C | |
| Rear Temperature | 230 - 245 | °C | |
| Middle Temperature | 240 - 255 | °C | |
| Front Temperature | 245 - 265 | °C | |
| Nozzle Temperature | 240 - 260 | °C | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 40.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 sp=62mm |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RANPELEN J-550S | Lotte Chemical Corporation | PP Random Copolymer | RANPELEN |
| TEREZ PA 6 7450 T GK 30 | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| Gallonprene® GP210-6510 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Sylvin 8826-65FUV Brown 7459 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ THERMOCOMP™ NF002 compound | SABIC Innovative Plastics | PC+ABS | LNP™ THERMOCOMP™ |