Styrolution PS 2600/2601
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | Styrolution PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ufuc7v_Styrolution-PS-2600-2601.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Styrolution PS 2600/2601 is a General Purpose Polystyrene product. It can be processed by foam extrusion or thermoforming and is available in Latin America or North America. Applications of Styrolution PS 2600/2601 include containers, decorative parts, foam, food contact applications and kitchenware. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Apparent Density | |||
| -- 1 | 0.59 to 0.64 | g/cm³ | |
| -- 2 | 0.62 to 0.67 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.4 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 75 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3170 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 44.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 3310 | MPa | ASTM D790 |
| Flexural Strength | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 21 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 90.6 | °C | |
| Vicat Softening Temperature | 96.1 | °C | ASTM D1525 3 |
| CLTE - Flow | 7.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (3.18 mm) | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1.00 mm, 1 MHz) | 2.50 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 4 | 1.590 | ASTM D542 | |
| Transmittance (550 nm) | 88.0 to 90.0 | % | ASTM D1003 |
| Optical Density - 400-700 nm avg. | 0.0460 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 191 to 274 | °C |
| Note Message | |
|---|---|
| 1 . | without external lubricant |
| 2 . | with external lubricant |
| 3 . | Rate B (120°C/h), Loading 1 (10 N) |
| 4 . | Sodium D line |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx FPE3A20CC | The Matrixx Group, Inc. | PE, Unspecified | Matrixx |
| TOTAL Polyethylene Lumicene® M 2710 EP (US) | TOTAL Refining & Chemicals | MDPE | TOTAL Polyethylene |
| TECHNYL® A 218 V15 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |
| OnForce™ LFT LF5200-5017 Grey | PolyOne Corporation | Polyolefin, Unspecified | OnForce™ LFT |
| LNP™ FARADEX™ AX88130 compound | SABIC Innovative Plastics | ABS | LNP™ FARADEX™ |