Durethan® BKV 50 H3.0 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UfC1Cy_DurethanBKV50H30000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 50 % glass fibers, injection molding, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.57 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | |||
| Vertical flow direction : 280°C, 3.00mm 1 | 0.85 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 3.00mm 2 | 0.050 | -- | % | ISO 2577 |
| Flow direction : 280°C, 3.00mm 3 | 0.16 | -- | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 3.00mm 4 | 0.020 | -- | % | ISO 2577 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 5.0 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.5 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 16800 | 10200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 225 | 140 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | 5.0 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 15500 | 9900 | MPa | ISO 178/A |
| Flexural Stress 6(23°C) | 360 | 230 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 3.0 | 5.0 | % | ISO 178/A |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behavior 8(> 1.00 mm) | passed | -- | ISO 3795 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GHR, 14-160, GF50 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 15 | 15 | kJ/m² | ISO 179/1eA |
| 23°C | 20 | 25 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 90 | 90 | kJ/m² | ISO 179/1eU |
| 23°C | 100 | 110 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | 15 | 15 | kJ/m² | ISO 180/1A |
| 23°C | 20 | 25 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 95 | 95 | kJ/m² | ISO 180/1U |
| 23°C | 95 | 100 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 205 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | > 200 | -- | °C | ISO 306/B50, ISO 306/B120 |
| Melting Temperature 9 | 222 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 2.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 7.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | UL 94 | |
| 3.20 mm | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 150x105x3mm, 80°C MT, 400 bar |
| 2 . | 150x105x3mm |
| 3 . | 150x105x3mm, 80°C MT, 400 bar |
| 4 . | 150x105x3mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | US-FMVSS302 |
| 9 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Staramide RX06027 | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| Xuchuan XCW-6100(T) | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Naxel PC40 | Custom Resins Group | PC | Naxel |
| Geon™ Vinyl Rigid Extrusion 87727 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Karina BLACK PVC COMPOUND 70900-48/1-F-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |