Order Products : sales@su-jiao.com
EXCELLOY DX220
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Techno Polymer Co, Ltd. |
| Trademark: | EXCELLOY |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Uelp7g_EXCELLOY-DX220.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EXCELLOY DX220 is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by injection molding and is available in Asia Pacific or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 30 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.60 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 85 | ASTM D785 | |
| R-Scale | 84 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 49.0 | MPa | ASTM D638 |
| Yield | 47.0 | MPa | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2260 | MPa | ASTM D790 |
| -- | 1870 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 76.5 | MPa | ASTM D790 |
| -- | 67.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 9.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | 88 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 85.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 72.0 | °C | ISO 75-2/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (ALL) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 2.0 to 5.0 | hr | |
| Rear Temperature | 190 to 260 | °C | |
| Middle Temperature | 190 to 260 | °C | |
| Front Temperature | 190 to 260 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NaturePlast PHE 008 | NaturePlast | PHA | NaturePlast |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 4213 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| Globalene® HP600S | Lee Chang Yung Chemical Industry Corp. | PP Homopolymer | Globalene® |
| OXNILON 66 ST 33GF | Oxford Polymers | Nylon 66 | OXNILON 66 |
| POCAN® T 7331 000000 | LANXESS GmbH | PBT+PET | POCAN® |