MARPOL® LDM 760
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Marco Polo International, Inc. |
| Trademark: | MARPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UeZ5gg_MARPOL-LDM-760.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Recommended Applications Injection molding, compounding, and industrial coatings Description MARPOL® LDM 760 is a low density polyethylene resin designed for tubular processing. This resin offers an excellent balance of processability and end use performance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| MD | 168 | MPa | |
| TD | 206 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 6.89 | MPa | |
| TD : Yield | 6.89 | MPa | |
| MD : Break | 20.7 | MPa | |
| TD : Break | 20.7 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break | 390 | % | |
| TD : Break | 690 | % | |
| Dart Drop Impact | 90 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 440 | g | |
| TD | 200 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 82 | ASTM D2457 | |
| Haze | 4.3 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® OBC 4975F | Teknor Apex Company | TPE | Telcar® |
| COPYLENE® CR030LN | Phillips 66 | PP Random Copolymer | COPYLENE® |
| Geon™ Vinyl Flexible K85 Natural & Black | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Kumho KNB 3430G | Korea Kumho Petrochemical Co., Ltd. | NBR | Kumho KNB |
| TECHNYL® B 230 GREY 1421 H | Solvay Engineering Plastics | Nylon 66/6 | TECHNYL® |