GAPEX® RPP20EC32NA
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | GAPEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UeLs6g_GAPEX-RPP20EC32NA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GAPEX®RPP20EC32NA is a polypropylene homopolymer (PP Homopoly) material, and its filler is 20% glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. GAPEX®The main features of the RPP20EC32NA are:
GAPEX®The typical application fields of RPP20EC32NA are: automobile industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| 23°C, 48 hours | 0.40 | % | ISO 294-4 |
| Vertical flow direction | 0.80 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 70.5 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 4.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 3300 | MPa | ISO 178 |
| Flexural Stress (23°C) | 80.3 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -40°C | 6.0 | kJ/m² | ISO 180/1A |
| 23°C | 7.3 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 155 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 143 | °C | ISO 75-2/A |
| Additional Information |
|---|
| The values listed as Molding Shrinkage, ISO 294-4, were tested in accordance with ISO 2577.Filler Content, ISO 3451: 20.0%Flammability, ISO 3795: 28 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 2605 | Covestro - Polycarbonates | PC | Makrolon® |
| Mirakutoran® TPU U385PSRU | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| SUMILITE® PVC VSS-HT210 | Sumitomo Bakelite Co., Ltd. | PVC, Unspecified | SUMILITE® PVC |
| WPP PP PPH2TF2-White | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| ColorRx® TPE-OM50A0RXTP | LTL Color Compounders, Inc. | TPE | ColorRx® |