SCLAIR® FP026-F
| Category: | LMDPE , Linear Medium Density Polyethylene |
| Manufacturer: | NOVA Chemicals |
| Trademark: | SCLAIR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Udba2C_SCLAIR-FP026-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SCLAIR® FP026-F is a Linear Medium Density Polyethylene material. It is available in North America for film extrusion. Important attributes of SCLAIR® FP026-F are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.926 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 76 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 25 µm, Blown Film | 234 | MPa | |
| 1% Secant, MD : 76 µm, Blown Film | 230 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 251 | MPa | |
| 1% Secant, TD : 76 µm, Blown Film | 260 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm, Blown Film | 11.0 | MPa | |
| MD : Yield, 76 µm, Blown Film | 12.0 | MPa | |
| TD : Yield, 25 µm, Blown Film | 12.0 | MPa | |
| TD : Yield, 76 µm, Blown Film | 12.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm, Blown Film | 490 | % | |
| MD : Break, 76 µm, Blown Film | 630 | % | |
| TD : Break, 25 µm, Blown Film | 710 | % | |
| TD : Break, 76 µm, Blown Film | 680 | % | |
| Dart Drop Impact | ASTM D1709A | ||
| 25 µm, Blown Film | 160 | g | |
| 76 µm, Blown Film | 450 | g | |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, Blown Film | 300 | g | |
| MD : 76 µm, Blown Film | 1100 | g | |
| TD : 25 µm, Blown Film | 750 | g | |
| TD : 76 µm, Blown Film | 1500 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 45°, 25.4 µm, Blown Film | 50 | ||
| 45°, 76.2 µm, Blown Film | 61 | ||
| Haze | ASTM D1003 | ||
| 25.4 µm, Blown Film | 14 | % | |
| 76.2 µm, Blown Film | 17 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Low Friction Puncture - Blown Film | Internal Method | ||
| 25.4 µm | 250 | J/cm | |
| 76.2 µm | 200 | J/cm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 MS 5 | RTP Company | Acetal (POM) Copolymer | RTP |
| Mirakutoran® TPU C565MNAT | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Hanwha Total PE EP31 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | LLDPE | Hanwha Total PE |
| HiFill® HDPE GF60 | Techmer Engineered Solutions | HDPE | HiFill® |
| Sylvin 4235-83 Blue 8484 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |