ELITE™ AT 6202
| Category: | EPE , Enhanced Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ELITE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UdGQ0v_ELITE-AT-6202.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ELITE™ AT 6202 Enhanced Polyethylene Resin is an enhanced LLDPE ethylene-octene copolymer from Dow. This grade is a fully formulated sealant resin designed for demanding applications where hot tack strength is a key requirement. Main Characteristics
Complies with:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.908 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.85 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Puncture Energy (25 µm) | 4.29 | J | Internal method |
| Film Puncture Force (25 µm) | 54.3 | N | Internal method |
| Film Puncture Resistance (25 µm) | 20.9 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 25 µm | 68.9 | MPa | ASTM D882 |
| 2% secant, TD : 25 µm | 77.2 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 7.93 | MPa | ASTM D882 |
| TD : Yield, 25 µm | 7.79 | MPa | ASTM D882 |
| MD : Break, 25 µm | 49.0 | MPa | ASTM D882 |
| TD : Break, 25 µm | 40.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 450 | % | ASTM D882 |
| TD : Break, 25 µm | 600 | % | ASTM D882 |
| Dart Drop Impact (25 µm) | 1000 | g | ASTM D1709B |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 25 µm | 210 | g | ASTM D1922 |
| TD : 25 µm | 430 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 106 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.4 µm) | 63 | ASTM D2457 | |
| Haze (25.4 µm) | 7.9 | % | ASTM D1003 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| VFFS Hot Tack Window 2 | 45°F (205-250) or 25°C (96-121) | Internal method |
| Extrusion instructions |
|---|
| Fabrication Conditions For Blown Film: Screw Size: 3.5in. (88.9 mm); 30:1ratio L/D Screw Type: DSBII Die Gap: 70mil (1.8 mm) Melt Temperature: 433°F (223°C) Output: 11.9 lb/hr/in. of die circumference Die Diameter: 8 in. Blow-Up Ratio: 2.5 to 1 Frost Line Height: 52 in. (1321 mm) |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | 2 mil coex film, 20/60/20 with MDPE core, sealant layer formulated with 10% LDPE and slip and AB. Tested on VFFS machine with 4 lbs fill weight, 0.25 second dwell time. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer N73B | Precision Polymer Engineering Ltd. | NBR | Precision Polymer |
| Bynel® 21E810 | DuPont Packaging & Industrial Polymers | EA | Bynel® |
| Derakane® Momentum 470-300 | Ashland Performance Materials | Vinyl Ester | Derakane® |
| Edgetek™ ET7400-8001 HG NC001 | PolyOne Corporation | PS (HIPS) | Edgetek™ |
| Generic Nylon 66+Nylon 6I/6T - Glass Fiber | Generic | Nylon 66+Nylon 6I/6T | Generic |