INNOPOL® PP CS 1-3810
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Inno-Comp Ltd. |
| Trademark: | INNOPOL® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ud1CzN_INNOPOL-PP-CS-1-3810.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INNOPOL® CS 1-3810 is a 10 % glass-fibre-filled polypropylene homopolymer compound. This grade is available in nature and custom coloured form. INNOPOL® CS 1-3810 is recommended for producing injection moulded products, where the required properties are high strength and stiffness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.970 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/5.0 kg) | 28.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.90 - 1.7 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 40.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 2.3 | kJ/m² | ISO 179/1eA |
| 23°C | 3.5 | kJ/m² | ISO 179/1eA |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Rear Temperature | 190 - 240 | °C | |
| Middle Temperature | 190 - 240 | °C | |
| Front Temperature | 190 - 240 | °C | |
| Processing (Melt) Temp | 210 - 250 | °C | |
| Mold Temperature | 10.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Hold pressure: 50 to 100 % of actual injection pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Elvax® 550A | DuPont Packaging & Industrial Polymers | EVA | Elvax® |
| Haysite BMC 24500 | Haysite Reinforced Plastics | Polyester, TS | Haysite BMC |
| Huafon EP625 | Huafon Group Co., Ltd. | Nylon 66 | Huafon |
| LNP™ THERMOCOMP™ XF006S compound | SABIC Innovative Plastics | Nylon, Unspecified | LNP™ THERMOCOMP™ |
| AKROMID® B3 1 S1 black (4124) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |