Generic TPO - Talc
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Uct8lk_Generic-TPO---Talc.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic TPO - Talc This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.992 - 1.08 | g/cm³ | ASTM D792 |
| 23°C | 1.00 - 1.23 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 - 30 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 0.010 - 1.3 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (23°C) | 59 - 75 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 18.8 - 30.3 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 12 - 70 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1300 - 3600 | MPa | ASTM D790 |
| 23°C | 1260 - 3500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.5 - 5.7 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 2.7 - 29 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 104 - 121 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 57.5 - 64.3 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 100 - 151 | °C | ISO 306 |
| CLTE - Flow | 7.4E-5 - 5.0E-4 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 57.2 - 100 | °C | |
| Drying Time | 1.5 - 3.0 | hr | |
| Rear Temperature | 193 - 238 | °C | |
| Middle Temperature | 204 - 238 | °C | |
| Front Temperature | 216 - 238 | °C | |
| Processing (Melt) Temp | 218 - 232 | °C | |
| Mold Temperature | 26.7 - 54.4 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic TPO - TalcThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DESLON™ 66 DSC210IR | DESCO Co., Ltd. | Nylon 66 | DESLON™ 66 |
| ELASTOSIL® R 500/70 | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| Karina GOLD MBATCH (SP31447) -E 45/ 56-GEN | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PEARLCOAT® 168K | Lubrizol Advanced Materials, Inc. | TPU-Polyether | PEARLCOAT® |
| Sylvin 4200-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |