HAIPLEN EP80 Y2
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | HAIPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UcpGcb_HAIPLEN-EP80-Y2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene copolymer medium viscosity, halogen free flame retardant UL94 V2, good mechanical properties. Designed for electrical applications requiring the compliance with RoHS decree (2002/95/CE). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 1.3 | % | Internal method |
| Flow direction | 1.3 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 35.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 40 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 70.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 90.0 | °C | IEC 60216 |
| Vicat Softening Temperature | |||
| -- | 138 | °C | ISO 306/A50 |
| -- | 92.0 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 1.00 mm | PLC 0 | UL 746 | |
| 1.60 mm | PLC 0 | UL 746 | |
| 3.00 mm | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 1.00 mm | PLC 3 | UL 746 | |
| 1.60 mm | PLC 2 | UL 746 | |
| 3.00 mm | PLC 1 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm | V-2 | UL 94 | |
| 1.60 mm | V-2 | UL 94 | |
| 3.00 mm | V-2 | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 825 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 850 | °C | IEC 60695-2-13 |
| Oxygen Index | 25 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 180 - 210 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Pre-heat Temperature: 70 to 80°CPre-heat Time: 1 hr |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2600H0 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| TOPAS® 8007F-600 | Topas Advanced Polymers, Inc. | COC | TOPAS® |
| Gallonprene® GP520-4009 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| LEXAN™ 505R resin | SABIC Innovative Plastics | PC | LEXAN™ |
| SCHULARENE™ N3102 | A. Schulman Europe | PLA | SCHULARENE™ |