Ebalta HFG plus / PUR 11
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ubgukb_Ebalta-HFG-plus-PUR-11.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This product is a polyurethane system. Applications
Properties
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Shore Hardness (Shore D) | 73 to 77 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 2300 to 2800 | MPa | ISO 178 |
| Flexural Stress | 18.0 to 22.0 | MPa | ISO 178 |
| Compressive Stress | 29.0 to 35.0 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 1.8 to 2.2 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Martens Temperature | 54 to 58 | °C | DIN 53458 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 22 | ||
| Resin | Mix Ratio by Weight: 100 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.03 to 1.07 | g/cm³ | |
| Viscosity (25°C) | 25 to 35 | Pa·s | |
| Curing Time (20°C) | 4.0 to 5.0 | hr | |
| Pot Life 1(20°C) | 7.0 to 9.0 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax 6331NW | LyondellBasell Industries | PP Homopolymer | Pro-fax |
| RESPOND™ EX4290 | LyondellBasell Industries | Polyolefin, Unspecified | RESPOND™ |
| Arak HDPE EX1 | Shazand (Arak) Petrochemical Corporation | HDPE | Arak HDPE |
| Eco-Solutions GP95T | MINIMA Technoloy Co. Ltd. | Biodeg Polymers | Eco-Solutions |
| PELPRENE™ P40H-05 | TOYOBO America, Inc. | TPEE | PELPRENE™ |