TECHNYL® A 238 V13 NATURAL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UbNt1y_TECHNYL-A-238-V13-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 66, reinforced with 13% of glass fibre, heat stabilized, with improved impact resistance, for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Molding Shrinkage | Internal Method | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 0.85 | -- | % | |
| Molding Shrinkage Isotropy | 0.850 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5500 | 3650 | MPa | ISO 527-2/1A |
| Tensile Stress (Yield) | 100 | 60.0 | MPa | ISO 527-2/1A |
| Tensile Strain (Yield) | 4.0 | 8.0 | % | ISO 527-2/1A |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 65 | 60 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | 8.0 | 10 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 228 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 263 | -- | °C | ISO 11357-3 |
| CLTE - Transverse (23 to 85°C) | 5.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® Homo 35.NA | Marco Polo International, Inc. | PP Homopolymer | MARPOL® Homo |
| Unichem 5514 | Colorite Polymers | PVC, Unspecified | Unichem |
| DIAREX® THF77 | PTT Global Chemical Public Company Limited | PS (GPPS) | DIAREX® |
| ExxonMobil™ HDPE HD 7925.30 | ExxonMobil Chemical | HDPE, UHMW | ExxonMobil™ HDPE |
| POLIMAXX HI650 | IRPC Public Company Limited | PS (HIPS) | POLIMAXX |