Flexirene® FH 56 A
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Flexirene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UbEI8I_Flexirene-FH-56-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Flexirene FH 56 A s a butene copolymer with medium density (C4-LLDPE), with antioxidants and processing aid, suitable for blown film extrusion. Film manufactured with Flexirene FH 56 A are characterised by a good rigidity and an optimum processability. Main Application Flexirene FH 56 A is recommended for the production of general purpose film in blend or in coextrusion with LDPE. It is also used for the production of nets because of its perfect balance between rigidity and processability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.934 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.4 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Thickness - Recommended / Available | 15 to 50µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 25 µm, Blown Film | 390 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 450 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm, Blown Film | 16.0 | MPa | |
| TD : Yield, 25 µm, Blown Film | 18.0 | MPa | |
| MD : Break, 25 µm, Blown Film | 40.0 | MPa | |
| TD : Break, 25 µm, Blown Film | 32.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm, Blown Film | 650 | % | |
| TD : Break, 25 µm, Blown Film | 800 | % | |
| Dart Drop Impact 1(25 µm, Blown Film) | 55 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 25.0 µm | 7.0 | kN/m | |
| TD : 25.0 µm | 60.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 117 | °C | ISO 306/A |
| Melting Temperature | 126 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 50 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 14 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTV-2 P-125 | Silicones, Inc. | Silicone Rubber, RTV-2 | RTV-2 |
| Bapolene® 4082NA | Bamberger Polymers, Inc. | PP Homopolymer | Bapolene® |
| EVALENE® PP PHJ0501 | JG Summit Petrochemical Corporation | PP Homopolymer | EVALENE® PP |
| DURACON® TW-31 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer+PE | DURACON® |
| Ensinger TECARAN™ ABS | Ensinger Inc. | ABS | Ensinger |