Panlite® ML-3206ZT
| Category: | PC , Polycarbonate |
| Manufacturer: | TEIJIN LIMITED |
| Trademark: | Panlite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ub2E49_PanliteML3206ZT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Injection Molding grade, Light diffusion grade, Weather resistance, Flame resistance |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 18.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Transverse flow : 4.00mm | 0.50 - 0.70 | % | Internal method |
| Flow : 4.00mm | 0.50 - 0.70 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 61.0 | MPa | ISO 527-2/50 |
| Fracture | 57.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2130 | MPa | ISO 178 |
| Flexural Stress 2 | 95.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 127 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.0 mm | V-2 | UL 94 | |
| 3.0 mm | V-2 | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.0 mm | 800 | °C | IEC 60695-2-12 |
| 3.0 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.0 mm | 850 | °C | IEC 60695-2-13 |
| 3.0 mm | 850 | °C | IEC 60695-2-13 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (3000 µm) | 77.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Monprene® MP-3017 | Teknor Apex Company | TPE | Monprene® |
| Amilan® CM3001-N | Toray Resin Company | Nylon 66 | Amilan® |
| Kumho PPG 6000 | Korea Kumho Petrochemical Co., Ltd. | POP | Kumho PPG |
| LNP™ THERMOCOMP™ FX10009 compound | SABIC Innovative Plastics Europe | PE, Unspecified | LNP™ THERMOCOMP™ |
| TECHNYL STAR® S 52G1 MX25 GREY 2408 | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR® |