Fiberfil® M-1812
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Fiberfil® Engineered Plastics Inc. |
| Trademark: | Fiberfil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UaoP68_Fiberfil-M-1812.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Fiberfil®M-1812 is a polypropylene homopolymer (PP Homopoly) material, and its filler is 45% talc filler. This product is available in North America,. Fiberfil®The main characteristics of the M-1812 are: homopolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18 mm | 0.50 - 0.70 | % | ASTM D955 |
| 6.35 mm | 0.70 - 0.90 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.030 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 - 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 4650 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 31.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 9.0 | % | ASTM D638 |
| Flexural Modulus - Tangent (23°C) | 4480 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 53.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 27 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 146 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 116 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 199 - 210 | °C | |
| Middle Temperature | 204 - 227 | °C | |
| Front Temperature | 182 - 199 | °C | |
| Nozzle Temperature | 182 - 193 | °C | |
| Processing (Melt) Temp | 199 - 232 | °C | |
| Mold Temperature | 32.2 - 71.1 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.00 - 0.689 | MPa |
| Injection instructions |
|---|
| Screw speed: Medium to Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PE XL8081TR | Sincerity Australia Pty Ltd. | PE, Unspecified | Sindustris PE |
| Sindustris PC HP5005A | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| UBE Polyamide Elastomer XPA 9040F1 | UBE Industries, Ltd. | TPA-ET | UBE Polyamide Elastomer |
| Colorite 88 Series 7588 | Colorite Polymers | PVC, Unspecified | Colorite 88 Series |
| ElectriPlast® EP-SS/66 | Integral Technologies, Inc. | Nylon 66 | ElectriPlast® |