PRL PPX-MF-FR3
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UadGbW_PRL-PPX-MF-FR3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PPX-MF-FR3 is a Polyphenylene Ether + PS (PPE+PS) product filled with mineral. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/11.6 kg) | 3.0 to 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 72.4 | MPa | |
| Break, 3.18 mm | 58.6 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, 3.18 mm | 3.5 | % | |
| Break, 3.18 mm | 8.0 | % | |
| Flexural Modulus (3.18 mm) | 3450 | MPa | ASTM D790 |
| Flexural Strength (Break, 3.18 mm) | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.4 | kJ/m² | ISO 179/2C |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 110 | J/m | ASTM D256 |
| 23°C | 8.4 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 110 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 104 | °C | |
| Vicat Softening Temperature | 127 | °C | ASTM D1525 1 |
| RTI Elec | UL 746 | ||
| 1.50 mm | 65.0 | °C | |
| 3.00 mm | 65.0 | °C | |
| RTI Imp | UL 746 | ||
| 1.50 mm | 65.0 | °C | |
| 3.00 mm | 65.0 | °C | |
| RTI Str | UL 746 | ||
| 1.50 mm | 65.0 | °C | |
| 3.00 mm | 65.0 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 249 to 299 | °C | |
| Middle Temperature | 260 to 304 | °C | |
| Front Temperature | 271 to 310 | °C | |
| Processing (Melt) Temp | 288 to 316 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILVER® ABS 313HF | Guangdong Silver Age Sci & Tech. Co., Ltd | ABS | SILVER® |
| Sinvicomp SIZ7408A | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| WPP TPO TPO-2470 UV RXF | Washington Penn Plastic Co. Inc. | TPO | WPP TPO |
| HiFill FR® PA6/6 GF33 FR HS L | Techmer Engineered Solutions | Nylon 66 | HiFill FR® |
| LEXAN™ HFD4412 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |