Fortron® 6450A6
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Celanese Corporation |
| Trademark: | Fortron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UadCtz_Fortron-6450A6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Fortron 6450A6 is a fiberglass reinforced, mineral filled alloy that exhibits improved wear and sliding properties versus standard Fortron compounds. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.58 | g/cm³ | ISO 1183 |
| Water Absorption (Saturation, 23°C) | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 90.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 11000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 130 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D1894 | ||
| Dynamic 1 | 0.31 | ASTM D1894 | |
| Dynamic 2 | 0.34 | ASTM D1894 | |
| Static 3 | 0.37 | ASTM D1894 | |
| Static 4 | 0.31 | ASTM D1894 | |
| With steel-dynamic 5 | 0.13 | ASTM D1894 | |
| With steel-static 6 | 0.16 | ASTM D1894 | |
| Wear Factor 7 | ASTM D3702 | ||
| 416 Stainless : 32°C | 164 | 10^-10 in³·min/ft·lb·hr | ASTM D3702 |
| C-1018 Steel : 49°C | 217 | 10^-10 in³·min/ft·lb·hr | ASTM D3702 |
| C-1018 Steel : 93°C | 300 | 10^-10 in³·min/ft·lb·hr | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 18 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 6.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, not annealed | 260 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 200 | °C | ISO 75-2/C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 - 140 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 290 - 300 | °C | |
| Middle Temperature | 310 - 320 | °C | |
| Front Temperature | 330 - 340 | °C | |
| Nozzle Temperature | 310 - 330 | °C | |
| Processing (Melt) Temp | 330 - 340 | °C | |
| Mold Temperature | 140 - 160 | °C | |
| Injection Pressure | 50.0 - 100 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 30.0 - 70.0 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 330 to 340°CZone 4 Temperature: 330 to 340°CFeed Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | vs Fortron 1140L4, 73°F, 5 lbf, 5 in |
| 2 . | vs Fortron 6165A4, 73°F, 5 lbf, 5 in |
| 3 . | vs Fortron 6165A4, 73°F, 5 lbf, 5 in |
| 4 . | vs Fortron 1140L4, 73°F, 5 lbf, 5 in |
| 5 . | 73°F, 5 lbf, 5 in |
| 6 . | 73°F, 5 lbf, 5 in |
| 7 . | 16 µ-in, PV2000, 40 psi, 50ft/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VESTOLIT® B 7521 Ultra | VESTOLIT GmbH & Co. KG | PVC Homopolymer | VESTOLIT® |
| Crastin® LW9020FR BK851 | DuPont Performance Polymers | PBT | Crastin® |
| Lion Idemitsu Composites PPS C-230SE | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |
| KEBAFORM® C 274 VT | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |
| Eleme NGL010FY | Eleme Petrochemical Company Ltd | LLDPE | Eleme |