Anjacom® 350-H/GF35
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Almaak International GmbH |
| Trademark: | Anjacom® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UaTSgm_Anjacom-350-H-GF35.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Anjacom® 350-H/GF35 is a Polyamide 66 (Nylon 66) material filled with 35% glass fiber. It is available in Europe. Important attributes of Anjacom® 350-H/GF35 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.41 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 5.0 | % | |
| Equilibrium, 23°C, 50% RH | 1.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 180 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 70 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 250 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 250 | °C | ISO 306/B50 |
| Melting Temperature | 260 | °C | DSC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 10 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STRANOX H-PP40%LFT | Oxford Polymers | PP Homopolymer | STRANOX |
| TAIRILITE AC3710 | Formosa Plastics Corporation | PC | TAIRILITE |
| Kapex C342 | Ginar Technology Co., LTD. | PC | Kapex |
| LUVOCOM® 6-8826 | Lehmann & Voss & Co. | Nylon 12 | LUVOCOM® |
| LNP™ THERMOCOMP™ LC006 compound | SABIC Innovative Plastics | PEEK | LNP™ THERMOCOMP™ |