PROTEQ™ H2UST4
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | PROTEQ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UZkORu_PROTEQ-H2UST4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PROTEQ™ H2UST4 is a 20% talc filled polypropylene homopolymer compound specifically developed for extrusion applications. It is a high viscosity grade with high stiffness and good weatherablity for outdoor applications. Applications include extruded profiles such as hydroponic pipes. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.90 to 1.5 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 77 | ||
| Shore D, 15 sec | 72 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 31.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 45 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2100 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 48.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 40 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 400 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 130 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 72.0 | °C | |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 550 | °C | AS/NZS 60695.2.12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 150 to 170 | °C | |
| Middle Temperature | 165 to 200 | °C | |
| Front Temperature | 170 to 210 | °C | |
| Processing (Melt) Temp | 190 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen RP5058 | PolyMirae | PP Random Copolymer | Moplen |
| NORYL™ WCA901 resin | SABIC Innovative Plastics | PPE+TPE | NORYL™ |
| LG PS 25SP(I) | LG Chem Ltd. | PS (GPPS) | LG PS |
| LNP™ VERTON™ RVL36SXS compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ VERTON™ |
| Vipel® K026-AAA-00 | AOC, L.L.C. | Vinyl Ester | Vipel® |