ASTALOY™ PC/ABS KMB
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UYPfgb_ASTALOY-PC-ABS-KMB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTALOY™ PC/ABS KMB is a flame retardant alloy of ABS and Polycarbonate and is designed to meet the stringent Underwriter's Laboratory UL94 V-0 test whilst offering improved heat resistance (i.e. Ball Indentation Temperature >125°C) and exceptional balance of impact toughness, product rigidity and mouldability. Typical applications include computer casing mouldings, electrical switchgear assemblies and whitegoods clothes dryer doors. Note: The letters "U" or "W" indicate additional UV stabilisation [ ie: ASTALOY™ PC/ABS KMBU ]. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 250°C/3.8 kg | 11 | g/10 min | |
| 260°C/5.0 kg | 24 | g/10 min | |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 58.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 190 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2450 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 85.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 560 | J/m | ASTM D256 |
| Gardner Impact (3.20 mm) | 75.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 125 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 131 | °C | |
| 1.8 MPa, Unannealed, 12.7 mm | 137 | °C | |
| Vicat Softening Temperature | 151 | °C | ASTM D1525 5 |
| CLTE - Flow | 7.2E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 960 | °C | AS/NZS 60695.2.12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 to 100 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 225 to 260 | °C | |
| Middle Temperature | 235 to 270 | °C | |
| Front Temperature | 245 to 280 | °C | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 4.0 to 8.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer V80D | Precision Polymer Engineering Ltd. | Fluorelastomer | Precision Polymer |
| TEREZ PA 6.6 7500 GF30 FL HF /2 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| MXSTEN® CV77518 | Westlake Chemical Corporation | Plastomer | MXSTEN® |
| Braskem PE SPB608 | Braskem America Inc. | LDPE | Braskem PE |
| HiFill FR® PA6/6 GB30 FR | Techmer Engineered Solutions | Nylon 66 | HiFill FR® |