Order Products : sales@su-jiao.com
Fibremod™ GB407HP
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Fibremod™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UYH3sk_Fibremod-GB407HP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fibremod GB407HP is a 40 % long glass fibre reinforced polypropylene grade intended for injection moulding and extrusion. The long glass fibres, chemically coupled to the polypropylene matrix, are providing outstanding mechanical properties such as high strength, high stiffness and excellent impact behaviour. Due to its excellent combination of properties this material can substitute in many applications other engineering plastics or metal alloys. A significant value of this material is the fact that it does not change its mechanical properties at humid conditions or water contact. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | Internal method | ||
| Vertical flow direction : 2.00mm | 0.60 | % | Internal method |
| Flow direction : 2.00mm | 0.10 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 132/10) | 123 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (1.00 mm) | 9000 | MPa | ISO 527-2 |
| Tensile Stress | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 8400 | MPa | ISO 178 |
| Flexural Stress | 200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 40 | kJ/m² | ISO 179/1eA |
| -20°C | 32 | kJ/m² | ISO 179/1eA |
| 23°C | 28 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 55 | kJ/m² | ISO 179/1eU |
| 23°C | 57 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -20°C | 34 | kJ/m² | ISO 180/1A |
| 23°C | 31 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 166 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 162 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 165 | °C | ISO 306/A |
| -- | 145 | °C | ISO 306/B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 40.0 - 80.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Feeding Temperatrue: 40 - 80 °CMass Temperature: 220 - 260 °CBack Pressure: Low to MediumScrew Speed: Low to MediumFlow Front Speed: 100 - 200 mm/s |
| Note Message | |
|---|---|
| 1 . | 150x80x2 |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vital-Line SHE6005 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| Braskem PE SPB208 | Braskem America Inc. | LDPE | Braskem PE |
| Clariant Nylon 6/6 6604-L | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| DIOSHY® XP-855 | DIOSHY Co.,Ltd. | SEBS+SBS | DIOSHY® |
| Sylvin 916VO-95 Brown 7137 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |